Highly ordered microporous films containing a polyolefin segment fabricated by the breath-figure method using well-defined polymethylene-b-polystyrene copolymers
其他题名利用呼吸图法和结构可控的聚亚甲基-b-聚苯乙烯嵌段共聚物制备的含有聚烯烃链段的高度有序微孔薄膜
Li J(李剑); Zhao QL(赵巧玲); Chen JZ(陈健壮); Li L(李磊); Huang J(黄晋); Ma Z(马志); Zhong YW(钟雅文)
2010
发表期刊Polym. Chem.
ISSN1759-9954
卷号1期号:2页码:164-167
摘要Highly ordered microporous films containing polyolefin segment were successfully fabricated via the breath-figure (BF) method using well-defined polymethylene-h-polystyrene (PM-h-PS) diblock copolymers in CS2 under a static humid condition. The effects of molecular weight of diblock copolymers, relative humid, fabrication method and temperature on the morphology of film are investigated. The honeycomb porous films with different pore size (1.2-2.5 mu m) were obtained by using PM-h-PS with different PM : PS ratio. The thick (7 mu m) and thin (2 mu m) films were fabricated via a different process. The film with a pothole-like structure was fabricated when using PM-h-PS with the shortest PS segment. Smaller satellite pores were found to surround the regular micropores of honeycomb films when the BF process was carried out at 28 degrees C.
学科领域高分子化学
部门归属中国科学院上海有机化学研究所; 厦门大学
URL查看原文
收录类别SCI
语种英语
WOS记录号WOS:000278602700006
引用统计
文献类型期刊论文
条目标识符http://ir.sioc.ac.cn/handle/331003/25385
专题分析化学研究室
通讯作者Li L(李磊); Ma Z(马志)
推荐引用方式
GB/T 7714
Li J,Zhao QL,Chen JZ,et al. Highly ordered microporous films containing a polyolefin segment fabricated by the breath-figure method using well-defined polymethylene-b-polystyrene copolymers[J]. Polym. Chem.,2010,1(2):164-167.
APA 李剑.,赵巧玲.,陈健壮.,李磊.,黄晋.,...&钟雅文.(2010).Highly ordered microporous films containing a polyolefin segment fabricated by the breath-figure method using well-defined polymethylene-b-polystyrene copolymers.Polym. Chem.,1(2),164-167.
MLA 李剑,et al."Highly ordered microporous films containing a polyolefin segment fabricated by the breath-figure method using well-defined polymethylene-b-polystyrene copolymers".Polym. Chem. 1.2(2010):164-167.
条目包含的文件
文件名称/大小 文献类型 版本类型 开放类型 使用许可
2010247.pdf(246KB) 开放获取--请求全文
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[李剑]的文章
[赵巧玲]的文章
[陈健壮]的文章
百度学术
百度学术中相似的文章
[李剑]的文章
[赵巧玲]的文章
[陈健壮]的文章
必应学术
必应学术中相似的文章
[李剑]的文章
[赵巧玲]的文章
[陈健壮]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。