题名: Synthesis of a novel perfluorooctylated polyacrylate and its application on cotton fabrics
其他题名: 新型的氟烷基丙烯酸酯的合成及对棉的整理
作者: Jiang WC(姜万超) ; Meng WD(孟卫东) ; Qing FL(卿凤翎)
通讯作者: 卿凤翎
刊名: J. Appl. Polym. Sci.
发表日期: 2005
卷: 98, 期:1, 页:222-226
收录类别: SCI
部门归属: 东华大学; 中国科学院上海有机化学所元素有机
英文摘要: A perfluorooctylated acrylate monomer (FAC) containing a urethane linkage was synthesized, and fluorinated polymers [perfluorooctylated polyacrylate (PFAC)] were obtained from the copolymerization of FAC with other acrylate monomers by emulsion polymerization. The size of the emulsion particles was about 40-60 nm. PFAC was applied to cotton fabrics by a pad-dry-cure process. The treated fabrics that were dried at 100 degrees C after being washed showed good water and oil repellency: the water repellency rating and the oil repellency rating were 100 and 5, respectively. Those dried at room temperature also showed water and oil repellency: the water repellency rating was 70 and the oil repellency rating was 3. (c) 2005 Wiley Periodicals, Inc.
语种: 英语
相关网址: 查看原文
WOS记录号: WOS:000231367700030
Citation statistics:
内容类型: 期刊论文
URI标识: http://ir.sioc.ac.cn/handle/331003/17537
Appears in Collections:中科院有机氟化学重点实验室_期刊论文

Files in This Item: Download All
File Name/ File Size Content Type Version Access License
2005082.pdf(121KB)----开放获取--View Download

Recommended Citation:
Jiang WC,Meng WD,Qing FL. Synthesis of a novel perfluorooctylated polyacrylate and its application on cotton fabrics[J]. J. Appl. Polym. Sci.,2005,98(1):222-226.
Service
Recommend this item
Sava as my favorate item
Show this item's statistics
Export Endnote File
Google Scholar
Similar articles in Google Scholar
[姜万超]'s Articles
[孟卫东]'s Articles
[卿凤翎]'s Articles
CSDL cross search
Similar articles in CSDL Cross Search
[姜万超]‘s Articles
[孟卫东]‘s Articles
[卿凤翎]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
Add to CiteULike Add to Connotea Add to Del.icio.us Add to Digg Add to Reddit
文件名: 2005082.pdf
格式: Adobe PDF
此文件暂不支持浏览
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Powered by CSpace